小直径芯样钻芯检测水泥基灌浆料抗压强度试验研究

doi:10.16046/j.cnki.issn2096-5680.2025.04.009

河北水利电力学院学报 ›› 2025, Vol. 35 ›› Issue (4): 51-59.DOI: 10.16046/j.cnki.issn2096-5680.2025.04.009

小直径芯样钻芯检测水泥基灌浆料抗压强度试验研究

李其廉^1,2, 卢雷¹

1.河北科技大学建筑工程学院,河北省石家庄市裕华区裕翔街26号 050018;
2.河北省岩土与结构体系防灾减灾技术创新中心,河北省石家庄市裕华区裕翔街26号 050018

收稿日期:2024-09-20 修回日期:2024-12-25 出版日期:2025-11-30 发布日期:2026-01-05
通讯作者: 卢雷(1999-),男,河北石家庄人,硕士研究生,主要研究方向:建筑结构的检测和加固。E-mail:2310762080@qq.com
作者简介:李其廉(1965-),男,河北邢台人,副教授,主要研究方向:建筑结构的检测、鉴定及加固。E-mail:695203421@qq.com
基金资助:
国家自然科学基金(51701026)

Experimental Study on Compressive Strength of Cement- based Grouting Material Using Small-diameter Core Samples

LI Qilian^1,2, LU Lei¹

1. School of Civil Engineering, Hebei University of Science and Technology, 050018, Shijiazhuang, Hebei, China;
2. Hebei Geotechnical and Structural System Disaster Prevention and Mitigation Technology Innovation Center, 050018, Shijiazhuang, Hebei, China

Received:2024-09-20 Revised:2024-12-25 Online:2025-11-30 Published:2026-01-05

摘要/Abstract

摘要： 为确定钢筋混凝土结构加固中水泥基灌浆料实体构件的抗压强度,根据《水泥基灌浆材料应用技术规范》(GB/T 50448-2015)中的要求,设计制作了高径比为1,直径为50、70mm的两种小直径芯样试件,开展小直径芯样钻芯法检测水泥基灌浆料抗压强度试验研究。结果表明:水泥基灌浆料标准试块和小直径芯样试件的抗压强度随龄期的增长而提高,前期抗压强度增长速率较快,后期增长速率减缓;70mm小直径芯样试件较50mm小直径芯样试件的抗压强度高,且其抗压强度离散性较小;基于最小二乘法,得到了50、70mm小直径芯样试件与水泥基灌浆料标准试块抗压强度之间的幂函数推算公式。综合考虑拟合效果和误差分析,建议采用70mm小直径芯样检测水泥基灌浆料抗压强度。

关键词: 水泥基灌浆料, 小直径芯样, 抗压强度, 最小二乘法, 幂函数

Abstract: In order to determine the compressive strength of cement-based grouting material components in strengthening reinforced concrete structures, two types of small-diameter core samples with a height-to-diameter ratio of 1 and diameters of 50 mm and 70 mm are designed and fabricated according to the requirements outlined in the “Technical Specification for the Application of Cement-Based Grouting Materials” (GB/T50448-2015). An experimental study on the compressive strength of cement-based grouting materials detected by the small-diameter core drilling method is carried out. The results indicate that the compressive strength of both standard specimens and small-diameter core samples increase with age, exhibiting a rapid growth rate in the early stages and a gradual slowdown in the later stages. The compressive strength of the 70 mm small-diameter core samples is higher than that of the 50 mm samples, with lower dispersion in compressive strength. Based on the least squares method, power function equations are derived to estimate the compressive strength relationships between the 50 mm and 70 mm small-diameter core samples and the standard specimens. Considering the fitting results and error analysis, it is recommended to use the 70 mm small-diameter core samples for assessing the compressive strength of cement-based grouting materials.

Key words: cement-based grouting material, small-diameter core sample, compressive strength, least squares method, power function

中图分类号:

李其廉, 卢雷. 小直径芯样钻芯检测水泥基灌浆料抗压强度试验研究[J]. 河北水利电力学院学报, 2025, 35(4): 51-59.

LI Qilian, LU Lei. Experimental Study on Compressive Strength of Cement- based Grouting Material Using Small-diameter Core Samples[J]. Hebei University of Water Resources and Electric E, 2025, 35(4): 51-59.

参考文献

[1] 张亮,严建军,李响.混凝土结构耐久性的研究综述[J].材料导报,2013,27(S1):294-297.
[2] MOSALLAM A, TAHA M M R, KIM J J, et al. Strength and ductility of RC slabs strengthened with hybrid high-performance composite retrofit system[J]. Engineering Structures, 2012(36):70-80.
[3] 李忠,左巍巍.高强无收缩水泥基灌浆料在核电设备安装中的应用[J].核动力工程,2011,32(2):141-144.
[4] 中华人民共和国住房和城乡建设部.水泥基灌浆材料应用技术规范:GB/T 50448-2015[S].北京:中国建筑工业出版社,2015.
[5] 中华人民共和国住房和城乡建设部.钻芯法检测混凝土强度技术规程:JGJ/T 384-2016[S].北京:中国建筑工业出版社,2016.
[6] 谷慧,姚继涛,刘嘉兴,等.50mm直径超小芯样检测混凝土抗压强度的分析建议[J].工业建筑,2023,53(S1):708-712+622.
[7] 李雪雪,孙彬,毛诗洋,等.钻芯法检测薄壁预制构件混凝土抗压强度的试验研究[J].建筑结构,2023,53(24):74-79.
[8] MOHAMED Taman, METWALLY Abd Elaty, REDA N Behiry. Codes applicability of estimating the FRC compressive strength by the core-drilling method[J]. Construction and Building Materials, 2022(330):127227.
[9] 吴体,肖承波.不同直径芯样钻芯检测混凝土抗压强度的试验研究[J].建筑科学,2021,37(3):46-51.
[10] MOSTAFA Kazemi, RAHMAT Madandoust, JORGE De Brito. Compressive strength assessment of recycled aggregate concrete using schmidt rebound hammer and core testing[J]. Construction and Building Materials, 2019(224):630-638.
[11] 刘梦溪.混凝土芯样高径比与强度换算系数关系研究[J].混凝土,2012(8):51-54.
[12] 陈海彬,卢建勇,李凯.钻芯法检测混凝土强度芯样尺寸效应的研究[J].混凝土,2014(3):141-143.
[13] 崔士起,孔旭文,林世乐,等.小高径比芯样混凝土抗压强度试验研究[J].建筑科学,2015,31(1):55-58.
[14] 全国水泥标准化技术委员会.水泥胶砂抗压强度检验方法(ISO法):GB/T 17671-2021[S].北京:中国标准出版社,2021.
[15] 中华人民共和国住房和城乡建设部.混凝土物理力学性能试验方法标准:GB/T 50081-2019[S].北京:中国建筑工业出版社,2019.

小直径芯样钻芯检测水泥基灌浆料抗压强度试验研究

Experimental Study on Compressive Strength of Cement- based Grouting Material Using Small-diameter Core Samples

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

编辑推荐

Metrics

[1]	路维, 任永旺, 徐虎南, 宋兴海, 金坎辉. 芦苇加筋土的轻型击实效果评价研究[J]. 河北水利电力学院学报, 2024, 34(2): 1-7.
[2]	丁鹏飞, 张振寰. 水泥稳定路基土力学特性研究[J]. 河北水利电力学院学报, 2021, 31(3): 58-61.